Semiconductor device and method for manufacturing the same

ABSTRACT

A method for manufacturing a semiconductor device is provided by follows. A fin is formed over a substrate. A spacer is formed on a sidewall of a first portion of the fin. An epitaxy feature is grown from a second portion of the fin that is in a position lower than the first portion of the fin, in which the forming the epitaxy feature is performed after the forming the spacer. The spacer is removed to expose the first portion of the fin. A gate stack is formed around the exposed first portion of the fin.

RELATED APPLICATIONS

This application claims priority to US provisional application No. 62/475,316, filed on Mar. 23, 2017, which is herein incorporated by reference.

BACKGROUND

Manufacturing of an integrated circuit (IC) has been driven by increasing the density of the IC formed in a semiconductor device. This is accomplished by implementing more aggressive design rules to allow a larger density of the IC device to be formed. Nonetheless, the increased density of IC devices, such as transistors, has also increased the complexity of processing semiconductor devices with decreased feature sizes.

BRIEF DESCRIPTION OF THE DRAWINGS

Aspects of the present disclosure are best understood from the following detailed description when read with the accompanying figures. It is noted that, in accordance with the standard practice in the industry, various features are not drawn to scale. In fact, the dimensions of the various features may be arbitrarily increased or reduced for clarity of discussion.

FIGS. 1-19 are cross-sectional views illustrating a semiconductor device at various stages during fabrication in accordance with some embodiments of the present disclosure; and

FIGS. 20-25 are cross-sectional views of semiconductor devices during fabrication in accordance with some embodiments of the present disclosure.

DETAILED DESCRIPTION

The following disclosure provides many different embodiments, or examples, for implementing different features of the provided subject matter. Specific examples of components and arrangements are described below to simplify the present disclosure. These are, of course, merely examples and are not intended to be limiting. For example, the formation of a first feature over or on a second feature in the description that follows may include embodiments in which the first and second features are formed in direct contact, and may also include embodiments in which additional features may be formed between the first and second features, such that the first and second features may not be in direct contact. In addition, the present disclosure may repeat reference numerals and/or letters in the various examples. This repetition is for the purpose of simplicity and clarity and does not in itself dictate a relationship between the various embodiments and/or configurations discussed.

Furthermore, spatially relative terms, such as “beneath,” “below,” “lower,” “above,” “upper” and the like, may be used herein for ease of description to describe one element or feature's relationship to another element(s) or feature(s) as illustrated in the figures. The spatially relative terms are intended to encompass different orientations of the device in use or operation in addition to the orientation depicted in the figures. The apparatus may be otherwise oriented (rotated 90 degrees or at other orientations) and the spatially relative descriptors used herein may likewise be interpreted accordingly.

Gate all around (GAA) transistor structures may be patterned by any suitable method. For example, the structures may be patterned using one or more photolithography processes, including double-patterning or multi-patterning processes. Generally, double-patterning or multi-patterning processes combine photolithography and self-aligned processes, allowing patterns to be created that have, for example, pitches smaller than what is otherwise obtainable using a single, direct photolithography process. For example, in one embodiment, a sacrificial layer is formed over a substrate and patterned using a photolithography process. Spacers are formed alongside the patterned sacrificial layer using a self-aligned process. The sacrificial layer is then removed, and the remaining spacers may then be used to pattern the GAA structure.

FIGS. 1-19 are cross-sectional views illustrating a semiconductor device at various stages during fabrication in accordance with some embodiments of the present disclosure. The semiconductor device includes any fin-based, multi-gate transistor. The semiconductor device may be included in a microprocessor, memory cell, and/or other integrated circuit device. FIGS. 1-18 have been simplified for the sake of clarity to better understand the inventive concepts of the present disclosure. Additional features can be added in the semiconductor device, and some of the features described below can be replaced or eliminated in other embodiments of the semiconductor device.

As shown in FIG. 1, a pad layer 104, a mask layer 106, and a patterned photoresist layer 108 are formed in sequence over a substrate 102. In some embodiments, the substrate 102 is a bulk silicon substrate, such as a silicon wafer. In some embodiments, the substrate 102 includes an elementary semiconductor, such as silicon or germanium in a crystalline structure; a compound semiconductor, such as silicon germanium, silicon carbide, gallium arsenic, gallium phosphide, indium phosphide, indium arsenide, and/or indium antimonide; or combinations thereof. In some embodiments, the substrate 102 includes a silicon-on-insulator (SOI) substrate. The SOI substrate is fabricated using separation by implantation of oxygen (SIMOX), wafer bonding, and/or other suitable methods. In some embodiments, the substrate 102 includes various doped regions and other suitable features.

The pad layer 104 is formed over the substrate 102 and in contact with the substrate 102, in which the pad layer 104 is formed by any suitable process to any suitable thickness. In some embodiments, the pad layer 104 includes silicon oxide and is formed by a chemical vapor deposition (CVD) or a thermal oxidation process, in which the thermal oxidation process is a dry or a wet process. In some embodiments, the silicon oxide can be formed by physical vapor deposition (PVD), atomic layer deposition (ALD), high density plasma CVD (HDPCVD), other suitable methods, and/or combinations thereof.

The mask layer 106 is formed over the pad layer 104 and in contact with the pad layer 104, in which the mask layer 106 serves as a hard mask. The mask layer 106 is formed by any suitable process to any suitable thickness. The mask layer 106 may include a material such as silicon nitride, silicon oxide, silicon oxynitride, silicon carbide, silicon carbon nitride, amorphous silicon, poly silicon, other suitable material, or combinations thereof. In some embodiments, the mask layer 106 includes silicon nitride and is formed by a CVD process. In some embodiments, the silicon nitride is formed by PVD, ALD, HDPCVD, other suitable methods, and/or combinations thereof.

Then, the patterned photoresist layer 108 is formed over the mask layer 106. In some embodiments, the patterning of the photoresist layer 108 includes photoresist coating, soft baking, mask aligning, exposing pattern, post-exposure baking, developing photoresist, and hard baking. Thereafter, the mask layer 106 and pad layer 104 are etched through the patterned photoresist layer 108 so as to expose underlying substrate 102. The exposed substrate 102 is then etched to a plurality of fins 112 a, 112 b, 112 c, and 112 d, in which the resulting structure is shown in FIG. 2. The etching process may include a wet etching process, a dry etching process, or a combination thereof. The fins 112 a-112 d may be formed by an etching process using a reactive ion etch (RIE) and/or other suitable process. In some embodiments, a hydrofluoric acid (HF) or buffered HF may be used to etch the pad layer 104 to expose the substrate 102 according to the pattern of the patterned photoresist layer 108. In some embodiments, a dry etching process used to etch the substrate 102 includes a chemistry including fluorine-containing gas. In furtherance of the example, the chemistry of the dry etch includes CF₄, SF₆, or NF₃. In some embodiments, the fins 112 a-112 d are formed by a double-patterning lithography (DPL) process. The DPL process is a method of constructing a pattern on a substrate by dividing the pattern into two interleaved patterns. The DPL process allows enhanced feature (e.g., fin) density. Various DPL methodologies may be used including double exposure (e.g., using two mask sets).

As shown in FIG. 3, a liner layer 114 is blanket formed over the substrate 102 and on the fins 112 a-112 d. In some embodiments, the liner layer 114 includes a dielectric material such as silicon nitride, silicon oxynitride, silicon carbide, or combinations thereof. In some embodiments, the liner layer 114 is formed as a conformal layer over the fins 112 a-112 d and the substrate 102.

As shown in FIG. 4, an isolation dielectric 118 is formed over the substrate 102 and the fins 112 a-112 d. The isolation dielectric 118 surrounds and isolates the fins 112 a-112 d. In some embodiments, the isolation dielectric 118 includes a dielectric material such as silicon oxide, silicon nitride, silicon oxynitride, low k materials, air gap, other suitable material, or combinations thereof. In some embodiments, the silicon oxide is deposited by a CVD process. In some embodiments, the silicon oxide is formed by PVD, ALD, HDPCVD, other suitable methods, and/or combinations thereof. The silicon oxide may be alternatively formed by a high aspect ratio process (HARP). In some embodiments, the isolation dielectric 118 may have a multi-layer structure. In some embodiments, a planarizing process is performed to remove excess isolation dielectric 118 until reaching the mask layer 106. In some embodiments, the planarizing process includes a chemical mechanical polishing (CMP) process. In some embodiments, the mask layer 106 serves as a polish stop layer for stopping the CMP process.

As shown in FIG. 5, an etching process is performed to recess the isolation dielectric 118 such that the fins 112 a-112 d protrudes over the isolation dielectric 118. The isolation dielectric 118 can be referred to as shallow trench isolation (STI) in some embodiments. The upper portions of the fins 112 a-112 d above isolation dielectric 118 can be referred to as channel regions 120 a, 120 b, 120 c and 120 d. In some embodiments, the etching process is used to etch back the isolation dielectric 118 of FIG. 4, so as to expose a portion of sidewalls 122 of the liner layer 114. The etching process may include a wet etching, a dry etching process, or a combination thereof. In some embodiments, diluted HF, SiCoNi (including HF and NH₃), or the like, may be used as the etchant.

As shown in FIG. 6, an etching process is performed to remove exposed portions of the liner layer 114 to expose upper portions of the fins 112 a-112 d above the isolation dielectric 118. That is, the channel regions 120 a-120 d are exposed. In some embodiments, the etching process performed to the liner layer 114 may include a wet etching, a dry etching process, or a combination thereof. In some embodiments, the isolation dielectric 118 has higher etch resistance to an etchant used in the etching process than that of the liner layer 114, and hence portions of liner layer 114 lower than a top surface of the isolation dielectric 118 can be protected from the etching process.

As shown in FIG. 7, a spacer layer 124 is blanket formed over the exposed fins 112 a-112 d, and thus sidewalls of the channel regions 120 a-120 d are covered with the spacer layer 124. Therefore, the spacer layer 124 can protect the channel regions 120 a-120 d from the subsequent processes, and hence the spacer layer 124 can be referred to as a protective layer enclosing the channel regions 120 a-120 d of the fins 112 a-112 d. In some embodiments, the spacer layer 124 includes a dielectric material, such as silicon nitride (SiN), silicon carbon nitride (SiCN) or silicon oxygen carbon nitride (SiOCN), which has different etch selectivity than that of the liner layer 114 so as to selectively etch the underlying liner layer 114 in a subsequent step. The spacer layer 124 is formed by any suitable process, such as, CVD, PVD, and ALD. In some embodiments, the deposition of the spacer layer 124 may be a conformal process.

As shown in FIG. 8, an etching process is performed to remove horizontal portions of the spacer layer 124, while remaining vertical portions of the spacer layer 124 on sidewalls of the fins 112 a-112 d to act as spacers. The etching of the spacer layer 124 may be, for example, anisotropic etching.

As shown in FIG. 9, the isolation dielectric 118 is etched back to expose portions of the liner layer 114. The etching process may include a wet etching, a dry etching process, or a combination thereof. The etching process may include a wet etching, a dry etching process, or a combination thereof. In some embodiments, diluted HF, SiCoNi (including HF and NH₃), or the like, may be used as the etchant. In some embodiments, the liner layer 114 has higher etch resistance to the etchant used in the etching back than that of the isolation dielectric 118, and hence the liner layer 114 can be protected from the etching back. Similarly, the spacer layer 124 has higher etch resistance to the etchant used in the etching back than that of the isolation dielectric 118, and hence the spacer layer 124 can be protected from the etching back. Since the sidewalls of the channel regions 120 a-120 d are covered by the spacer layer 124 and top surfaces of the channel regions 120 a-120 d are covered by the pad layer 104 and mask layer 106, the channel regions 120 a-120 d can be protected from the etching back.

As shown in FIG. 10, an etching process is performed to remove the exposed portions of the liner layer 114 to expose the bottom portions of the fins 112 a-112 d below the spacer layer 124, in which the bottom portions of the fins 112 a, 112 b, 112 c, and 112 d below the spacer layer 124 can be referred to as source regions 125 a, 125 b, 125 c, and 125 d. In some embodiments, the etching process performed to the liner layer 114 may include a wet etching, a dry etching process, or a combination thereof. In some embodiments, the isolation dielectric 118 has higher etch resistance to an etchant used in the etching process than that of the liner layer 114, and hence portions of liner layer 114 lower than a top surface of the isolation dielectric 118 can be protected from the etching process. Similarly, the spacer layer 124 has higher etch resistance to the etchant used in the etching back than that of the liner layer 114, and hence the spacer layer 124 can be protected from the etching back. Since the sidewalls of the channel regions 120 a-120 d are covered by the spacer layer 124 and the top surfaces of the channel regions 120 a-120 d are covered by the pad layer 104 and mask layer 106, the channel regions 120 a-120 d can be protected from the etching back.

As shown FIG. 11, epitaxy source features 126 are grown from the source regions 125 a-125 d of the fins 112 a-112 d (e.g., the exposed portions of the fins 112 a-112 d) using an epitaxy or epitaxial (epi) process. That is, the epitaxy source feature 126 is epitaxially grown from the bottom portions of the fins 112 a-112 d, and the epitaxy source feature 126 surrounds the bottoms of the fins 112 a-112 d. The epitaxy process may include CVD deposition techniques (e.g., vapor-phase epitaxy (VPE) and/or ultra-high vacuum CVD (UHV-CVD)), molecular beam epitaxy, and/or other suitable processes. The epitaxy process may use gaseous and/or liquid precursors, which interact with the composition (e.g., silicon) of the fins 112 a-112 d. In some embodiments, the epitaxy source feature 126 is made of boron-doped silicon germanium (SiGeB) or silicon phosphide (SiP), and the epitaxy source feature 126 serves as a source electrode for a field effect transistor (FET). In some embodiments, the epitaxy source feature 126 includes facets F1, F2 and F3. The facets F1 are upward facing facets, the facets F2 are vertical facets, and the facets F3 are downward facing facets. In some embodiments, the facets F1 and F3 may be on (111) planes of the epitaxy source feature 126. In some embodiments, the facets F2 may be on (110) planes of the epitaxy source feature 126.

Furthermore, since the channel regions 120 a-120 d are formed prior to the growth of the epitaxy source features 126, the channel regions 120 a-120 d may be not susceptible to the quality of the epitaxy source features 126. For example, if thick epitaxy source features 126 are desired, defects such as high surface roughness of the epitaxy source features 126 may be formed, which would adversely affect epitaxy growth of channel regions if the channel regions are grown after the growth of the thick epitaxy source features 126. However, the channel regions 120 a-120 d are not susceptible to the defects of the thick epitaxy source features 126 because the channel regions 120 a-120 d are formed prior to formation of these defects. In some embodiments, since the channel regions 120 a-120 d are formed in advance, the surface roughness of the epitaxy source features 126 does not affect the surface roughness of the channel regions 120 a-120 d. Therefore, surface roughness of the channel regions 120 a-120 d is less than surface roughness of the epitaxy source features 126 in some embodiments. As a result, improved qualities of the channel regions 120 a-120 d can be obtained even if growth of the epitaxy source features 126 induces defects.

As shown in FIG. 12, another isolation dielectric 127 is formed to fill trenches between any two adjacent of the fins 112 a-112 d, so that the epitaxy source features 126 and the spacer layer 124 are covered with the isolation dielectric 127. Thereafter, a planarizing process is performed to remove excess isolation dielectric 127 until reaching the mask layer 106. In some embodiments, the planarizing process includes a CMP process. In some embodiments, the mask layer 106 serves as a polish stop layer for stopping the CMP process.

As shown in FIG. 13, the isolation dielectric 127 is etched back to expose the spacer layer 124. After the isolation dielectric 127 is etched back, the isolation dielectric is recessed, in which the epitaxy source features 126 are covered with the isolation dielectric 127. That is, the process of etching back the isolation dielectric 127 stops before the epitaxy source features 126 is exposed. The etching process may include a wet etching, a dry etching process, or a combination thereof. The etching process may include a wet etching, a dry etching process, or a combination thereof. In some embodiments, diluted HF, SiCoNi (including HF and NH₃), or the like, may be used as the etchant. In some embodiments, stopping the process of etching back can be achieved by controlling the etching time or the etching depth. In some embodiments, the spacer layer 124 has higher etch resistance to the etchant used in the etching back than that of the isolation dielectric 118, and hence the spacer layer 124 can be protected from the etching back. Since the sidewalls of the channel regions 120 a-120 d are covered by the spacer layer 124 and the top surfaces of the channel regions 120 a-120 d are covered by the pad layer 104 and mask layer 106, the channel regions 120 a-120 d can be protected from the etching back.

Thereafter, one or more etching processes are performed to remove the spacer layer 124 and the mask layer 106, and the resulting structure is shown in FIG. 14. The etching process may include a wet etching, a dry etching process, or a combination thereof. An exemplary method of removing the etching process is wet etching which is able to selectively remove silicon nitride, and this wet etching utilizes hot (approximately 145° C.-180° C.) phosphoric acid (H₃PO₄) solutions with water. In some embodiments, the isolation dielectric 127 and pad layer 104 has higher etch resistance to the etchant used in the etching process than that of the spacer layer 124, and hence the isolation dielectric 118 and pad layer 104 can be not removed by the etching process. After the etching process, channel regions 120 a-120 d of the fins 112 a-112 d are exposed.

As shown in FIG. 15, a gate dielectric layer 130 is blanket formed over the exposed fins 112 a, 12 b, 112 c, and 112 d, and thus the channel regions 120 a-120 d are enclosed by with the gate dielectric layer 130. In some embodiments, the gate dielectric layer 130 includes an interfacial layer (IL) which includes, for example, a silicon oxide (SiO₂) layer. In some embodiments, the IL includes HfSiO or SiON. In some embodiments, the IL is formed by ALD, CVD, thermal oxidation, wet oxidation, radical oxidation (RadOx) or combinations thereof. In some embodiments, the IL includes a chemical SiO₂ layer with hydroxyl groups. In some embodiments, the gate dielectric layer 130 includes a high-k (HK) dielectric layer formed over the IL by ALD, CVD, metal organic CVD (MOCVD), PVD, combinations thereof, or other suitable techniques. In some embodiments, the HK dielectric layer includes a binary or ternary high-k film such as HfOx. In some embodiments, the HK dielectric layer includes other HK dielectrics such as LaO, AlO, ZrO, TiO, Ta₂O₅, Y₂O₃, SrTiO₃ (STO), BaTiO₃ (BTO), BaZrO, HfZrO, HfLaO, HfSiO, LaSiO, AlSiO, HfTaO, HfTiO, (Ba,Sr)TiO₃ (BST), Al₂O₃, Si₃N₄, oxynitrides, or other suitable materials.

As shown in FIG. 16, a metal gate 132 is formed into recesses of the gate dielectric layer 130, and a planarization process, such as a CMP process, is then performed to remove the excess metal gate 132 until reaching the gate dielectric layer 130. Therefore, the metal gate 132 is around the channel regions 120 a-120 d of the fins 112 a-112 d, and thus each channel region is enclosed by the metal gate 132, so as to form a vertical gate-all-around (VGAA) device. The metal gate 132 and the gate dielectric layer 130 can be in combination referred to as a gate stack. If the gate dielectric layer 130 is a high-k dielectric layer, the gate stack can be referred to as a high-k metal gate (HKMG) stack. In addition, portions of the fins 112 a-112 d that are covered with the HKMG stack and the epitaxy source features 126 are formed as one piece. In some embodiments, the metal gate 132 includes, for example work function (WF) layers, barrier layers, fill metal layer, liner layer, wetting layer, and adhesion layer. In some embodiments, the metal gate 132 is formed by ALD, PVD, CVD, or other suitable process. For example, a Ti layer may be deposited to function as a wetting layer for a subsequent metal filling, in which the Ti layer may be formed by PVD or other suitable process.

As shown in FIG. 17, an etching process is performed to remove upper portions of the gate dielectric layer 130 and the metal gate 132 such that tops of the fins 112 a-112 d protrude from the HKMG stack including the gate dielectric layer 130 and the metal gate 132. The protruding tops of the fins 112 a-112 d can be referred to as drain regions 133 a, 133 b, 133 c, and 133 d. The etching process may include a wet etching, a dry etching process, or a combination thereof. In addition, the etching process includes removing the pad layer 104 (see FIG. 16).

As shown in FIG. 18, epitaxy drain features 134 are grown from the drain regions 133 a-133 d of the fins 112 a-112 d (e.g., the exposed portions of the fins 112 a-112 d) using an epitaxy process. The channel regions 120 a-120 d are between the corresponding epitaxy source features 126 and the corresponding epitaxy drain features 134. The epitaxy process may include CVD deposition techniques (e.g., vapor-phase epitaxy (VPE) and/or ultra-high vacuum CVD (UHV-CVD)), molecular beam epitaxy, and/or other suitable processes. The epitaxy process may use gaseous and/or liquid precursors, which interact with the composition (e.g., silicon) of the fins 112 a-112 d. In some embodiments, the top surfaces of the fins 112 a-112 d are covered with the epitaxy drain features 134. In some embodiments, the epitaxy source features 126 and the epitaxy drain features 134 are made of the same material. In some embodiments, the epitaxy drain features 134 are made of boron-doped silicon germanium (SiGeB) or silicon photonics (SIP), and the epitaxy drain features 134 serve drain electrodes for the FETs. In some embodiments, the epitaxy drain feature 134 includes facets F4 and F5. For example, the facets F4 are upward facing facets, and the facets F5 are downward facing facets. In some embodiments, the facets F4 and F5 may be on (111) planes of the epitaxy drain feature 134.

As shown in FIG. 19, an interlayer dielectric (ILD) layer 136 is formed to cover the epitaxy drain features 134, the gate dielectric layer 130 and the metal gate 132, and a planarization process (e.g. CMP) is performed to the ILD layer 136 until reaching the epitaxy drain features 134. In some embodiments, the ILD layer 136 may include silicon oxide, silicon nitride, silicon oxynitride, tetraethoxysilane (TEOS), phosphosilicate glass (PSG), borophosphosilicate glass (BPSG), low-k dielectric material, and/or other suitable dielectric materials. Examples of low-k dielectric materials include, but are not limited to, fluorinated silica glass (FSG), carbon doped silicon oxide, amorphous fluorinated carbon, parylene, bis-benzocyclobutenes (BCB), or polyimide. The ILD layer 136 may be formed using, for example, CVD, ALD, spin-on-glass (SOG) or other suitable techniques.

Although the epitaxy source features 126 are formed as including the facets F1, F2 and F3, as depicted in FIG. 19, the epitaxy source features 126 can be formed in other shapes. For example, FIGS. 20-25 are cross-sectional views of semiconductor devices during fabrication in accordance with some embodiments of the present disclosure, in which FIGS. 20-25 illustrate various epitaxy source features 126 with different shapes. As shown in FIGS. 20, the epitaxy source features 126 are formed in diamond shapes with sloped sidewalls. As shown in FIG. 21, the epitaxy source features 126 are formed in cylinders with vertical sidewalls. As shown in FIG. 22, the epitaxy source features 126 are formed in barrels with convex sidewalls. As shown in FIG. 23, the epitaxy source features 126 are formed in diamond shapes that are similar with the shapes illustrated in FIG. 20, in which the epitaxy source features 126 are grown from the fins until the epitaxy source features 126 are merged. As shown in FIG. 24, the epitaxy source features 126 are formed in diamond shapes that are similar with the shapes illustrated in FIG. 11, in which the epitaxy source features 126 are grown from the fins until the epitaxy source features 126 are merged.

As shown in FIG. 25, operations respectively performed before FIG. 25 are as described in FIGS. 1-10, and hence they are not repeated herein. First bottom portions of fins 112 a-112 d under the channel regions 120 a-120 d are removed, and second bottom portions 113 a, 113 b, 113 c, and 113 d of the fins 112 a-112 d under the channel regions 120 a-120 d remain, such that openings 138 are formed in the second bottom portions 113 a-113 d of fins 112 a-112 d. In addition, the upper portions of the fins 112 a-112 d are supported by the second bottom portions 113 a, 113 b, 113 c, and 113 d of the fins 112 a-112 d, and the upper portions of the fins 112 a-112 d has first surfaces S1 and the substrate 102 has a second surface S2 facing the first surfaces S1.

During the epitaxial process of the epitaxy source feature 126, the epitaxy source feature 126 is grown in the opening 138 and between the first surface S1 and the second surface S2. That is, a first portion 126 a of the epitaxy source feature 126 is epitaxially grown from the first surface S1, and a second portion 126 b of the epitaxy source feature 126 is epitaxially grown from the second surface S2. In some embodiments, the first portion 126 a and the second portion 126 b are merged with each other. In some embodiments, there exists a distinguishable interface between the first portion 126 a and the second portion 126 b. In alternative embodiments, the first portion 126 a and the second portion 126 b may be merged with no distinguishable interface thereb etween.

As described above, in the semiconductor device, since the channel regions are formed prior to the growth of the epitaxy source features, the channel regions are not susceptible to the quality of the epitaxy source features. For example, if defects such as high surface roughness of the epitaxy source features are formed, the channel regions are not susceptible to the defects of the epitaxy source features because the channel regions are formed prior to formation of these defects. Furthermore, since the channel regions are formed in advance, the surface roughness of the epitaxy source features does not affect the surface roughness of the channel regions. Therefore, surface roughness of the channel regions is less than surface roughness of the epitaxy source features. As a result, improved qualities of the channel regions can be obtained even if growth of the epitaxy source features induces defects.

According to various embodiments of the present disclosure, a method for manufacturing a semiconductor device is provided by follows. A fin is formed over a substrate. A spacer is formed on a sidewall of a first portion of the fin. An epitaxy feature is grown from a second portion of the fin that is in a position lower than the first portion of the fin, in which the forming the epitaxy feature is performed after the forming the spacer. The spacer is removed to expose the first portion of the fin. A gate stack is formed around the exposed first portion of the fin.

According to various embodiments of the present disclosure, a method for manufacturing a semiconductor device is provided by follows. At least one fin is formed over a substrate. At least one protective layer is formed to enclose a channel region of the fin. At least one epitaxy feature grown from a source region of the fin, wherein the source region is under the enclosed channel region. The protective layer is removed to expose the channel region after the growing the epitaxy feature. A gate stack is formed to enclose the exposed channel region.

According to various embodiments of the present disclosure, a semiconductor device includes a substrate, a fin, a first epitaxy feature, and a gate stack. The fin is over the substrate. The first epitaxy feature surrounds a first portion of the fin. A gate stack surrounds a second portion of the fin and is over the first epitaxy feature, in which surface roughness of the second portion of the fin is less than that of the first epitaxy feature.

The foregoing outlines features of several embodiments so that those skilled in the art may better understand the aspects of the present disclosure. Those skilled in the art should appreciate that they may readily use the present disclosure as a basis for designing or modifying other processes and structures for carrying out the same purposes and/or achieving the same advantages of the embodiments introduced herein. Those skilled in the art should also realize that such equivalent constructions do not depart from the spirit and scope of the present disclosure, and that they may make various changes, substitutions, and alterations herein without departing from the spirit and scope of the present disclosure. 

1. A method for manufacturing a semiconductor device, comprising: forming a fin over a substrate; forming a spacer on a sidewall of a first portion of the fin; growing an epitaxy feature from a second portion of the fin that is in a position lower than the first portion of the fin, wherein the forming the epitaxy feature is performed after the forming the spacer; removing the spacer to expose the first portion of the fin; and forming a gate stack around the exposed first portion of the fin.
 2. The method of claim 1, further comprising: forming a liner layer to cover the fin; and removing a first portion of the liner layer to expose the second portion of the fin, wherein forming the epitaxy feature is performed after the removing the first portion of the liner layer.
 3. The method of claim 2, wherein the spacer remains on the first portion of the fin during the removing the first portion of the liner layer.
 4. The method of claim 2, wherein the removing the first portion of the liner layer is performed by using an etching process, and wherein the spacer has higher etch resistance to an etchant used in the etching process than that of the liner layer.
 5. The method of claim 2, wherein the liner layer is formed prior to the forming the spacer, and the method further comprises: removing a second portion of the liner layer to expose the first portion of the fin, wherein the forming the spacer is performed after the removing the second portion of the liner layer, and the removing the first portion of the liner layer is performed after the forming the spacer.
 6. The method of claim 5, further comprising: forming an isolation dielectric over the substrate to cover the liner layer; and performing a first etching process to recess the isolation dielectric to expose the second portion of the liner layer.
 7. The method of claim 6, wherein the first portion of the liner layer is covered with the isolation dielectric, and the method further comprises: performing a second etching process to remove the second portion of the liner layer, wherein the isolation dielectric has higher etch resistance to an etchant used in the second etching process than that of the liner layer.
 8. The method of claim 1, further comprising: forming an isolation dielectric over the substrate to cover the spacer and the epitaxy feature; and recessing the isolation dielectric to expose the spacer prior to the removing the spacer.
 9. The method of claim 8, wherein the recessing the isolation dielectric is performed by using an etching process, and wherein the spacer has higher etch resistance to an etchant used in the etching process than that of the isolation dielectric.
 10. The method of claim 1, further comprising: forming an opening in the second portion of the fin, wherein epitaxy feature is grown in the opening in the second portion.
 11. A method for manufacturing a semiconductor device, comprising: forming at least one fin over a substrate; forming at least one protective layer to enclose a channel region of the fin; growing at least one epitaxy feature from a source region of the fin, wherein the source region is under the enclosed channel region; removing the protective layer to expose the channel region after the growing the epitaxy feature; and forming a gate stack to enclose the exposed channel region.
 12. The method of claim 11, further comprising: forming an isolation dielectric around the epitaxy feature prior to the removing the protective layer, wherein the isolation dielectric has higher etch resistance to the removing the protective layer than that of the protective layer.
 13. The method of claim 12, wherein the forming the isolation dielectric comprises: forming the isolation dielectric around the protective layer and the epitaxy feature; and recessing the isolation dielectric such that the protective layer is exposed.
 14. The method of claim 13, wherein the recessing the isolation dielectric stops before the epitaxy feature is exposed.
 15. The method of claim 11, wherein the growing the epitaxy feature comprises: growing a plurality of the epitaxy features from a plurality of the fins until the epitaxy features are merged.
 16. The method of claim 11, wherein the fin comprises a mask layer thereon, and the removing the protective layer removes the mask layer. 17-20. (canceled)
 21. A method for manufacturing a semiconductor device, comprising: forming at least one fin over a substrate; growing a first epitaxy feature from a first portion of the fin, such that a second portion of the fin protrudes above the first epitaxy feature; forming a gate stack to surround the second portion of the fin; and growing a second epitaxy feature from the second portion of the fin.
 22. The method of claim 21, further comprising: forming an isolation dielectric in contact with the first epitaxy feature, such that the first epitaxy feature is between the fin and the isolation dielectric.
 23. The method of claim 21, wherein forming the fin comprises: forming a third portion of the fin protruding from the substrate, wherein the first epitaxy feature is grown in a position higher than the third portion.
 24. The method of claim 21, further comprising: forming a spacer covering the second portion of the fin prior to growing the first epitaxy feature. 